چکیده:

Pollucite zeolite as one of the alumina silicate zeolites with high absorption ability was synthesized in this study. Synthesis of this zeolite was performed with three gelformulasof1Al2O3:3Na2O:0.4Cs2O:10.8SiO2:400H2O, 1Al2O3:6Na2O:0.8Cs2O:10.8SiO2:400H2O and 1Al2O3:9Na2O:1.2Cs2O:10.8SiO2:400H2O with three different heating time varied from 4 to10 days. Higher crystallinity of the synthesized zeolite powder was the main object of this work. According to the XRD results, the best zeolite was synthesized using the synthesis time of 7 daysat 100°C with further 24 h aging